Co-leaching of Li, Fe, Al, and Cu from active materials of LFP batteries

Capa

Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

Co-leaching of the cathode and anode materials of lithium iron phosphate (LFP) batteries was studied. It was determined that the nature of mineral acid (nitric, sulfuric, hydrochloric) affects the degree of leaching of Li, Fe, Al, and Cu. Hydrochloric acid was chosen as the most suitable leaching agent. The effect of the following parameters of the leaching of active materials was investigated: process duration, temperature, hydrochloric acid concentration, and solid : liquid ratio. For complete leaching of copper, hydrogen peroxide was used as an oxidizing agent. The conditions for the most complete extraction of target elements were found to be 25°C, 2 h, 2 M hydrochloric acid solution, 0.05 M H2O2 solution, solid : liquid ratio 1 : 50. The possibility of sufficiently complete leaching of the main elements from spent LFP batteries at room temperature was demonstrated.

Sobre autores

A. Salomatin

Kurnakov Institute of General and Inorganic Chemistry RAS; National Research University Higher School of Economics

Email: yz@igic.ras.ru
Rússia, Moscow, 119071; Moscow, 109028

I. Zinov’eva

Kurnakov Institute of General and Inorganic Chemistry RAS

Email: yz@igic.ras.ru
Rússia, Moscow, 119071

Yu. Zakhodyaeva

Kurnakov Institute of General and Inorganic Chemistry RAS

Autor responsável pela correspondência
Email: yz@igic.ras.ru
Rússia, Moscow, 119071

A. Voshkin

Kurnakov Institute of General and Inorganic Chemistry RAS

Email: yz@igic.ras.ru
Rússia, Moscow, 119071

Bibliografia

  1. The United Nations // 2015.
  2. The Global EV Outlook // 2023. https://www.iea.org/reports/global-ev-outlook-2023
  3. Fallah N., Fitzpatrick C. // J. Energy Storage. 2023. V. 68. P. 107740. https://doi.org/10.1016/j.est.2023.107740
  4. Fan T., Liang W., Guo W. et al. // J. Energy Storage. 2023. V. 71. P. 108126. https://doi.org/10.1016/j.est.2023.108126
  5. Hu J., Huang W., Yang L. et al. // Nanoscale. 2020. V. 12. № 28. P. 15036. https://doi.org/10.1039/D0NR03776A
  6. Yao Y., Zhu M., Zhao Z. et al. // ACS Sustain. Chem. Eng. 2018. V. 6. № 11. P. 13611. https://doi.org/10.1021/acssuschemeng.8b03545
  7. Davis K., Demopoulos G.P. // RSC Sustain. 2023. V. 1. № 8. P. 1932. https://doi.org/10.1039/D3SU00142C
  8. Dobó Z., Dinh T., Kulcsár T. // Energy Reports. 2023. V. 9. P. 6362. https://doi.org/10.1016/j.egyr.2023.05.264
  9. Zhou L.-F., Yang D., Du T. et al. // Front. Chem. 2020. V. 8. https://doi.org/10.3389/fchem.2020.578044
  10. Vasconcelos D. da S., Tenório J.A.S., Botelho Junior A.B. et al. // Metals (Basel). 2023. V. 13. № 3. P. 543. https://doi.org/10.3390/met13030543
  11. Aaltonen M., Peng C., Wilson B.P. et al. // Recycling. 2017. V. 2. № 4. P. 20. https://doi.org/10.3390/recycling2040020
  12. Song D., Wang T., Liu Z. et al. // J. Environ. Chem. Eng. 2022. V. 10. № 1. P. 107102. https://doi.org/10.1016/j.jece.2021.107102
  13. Федорова М.И., Левина А.В., Заходяева Ю.А. и др. // Журн. неорган. химии. 2022. Т. 67. № 7. С. 1000. https://doi.org/10.31857/S0044457X22070091
  14. Кожевникова А.В., Уварова Е.С., Милевский Н.А. и др. // Теорет. основы хим. технологии. 2023. Т. 57. № 5. С. 553. https://doi.org/10.31857/S0040357123050111
  15. Nicol M.J. // Hydrometallurgy. 2020. V. 193. P. 105328. https://doi.org/10.1016/j.hydromet.2020.105328
  16. Huang Z., Chen T., Zhou Y. et al. // Processes. 2020. V. 8. № 12. P. 1534. https://doi.org/10.3390/pr8121534
  17. Li H., Xing S., Liu Y. et al. // ACS Sustain. Chem. Eng. 2017. V. 5. № 9. P. 8017. https://doi.org/10.1021/acssuschemeng.7b01594
  18. Liu W., Li K., Wang W. et al. // Can. J. Chem. Eng. 2023. V. 101. № 4. P. 1831. https://doi.org/10.1002/cjce.24617
  19. Gradov O.M., Zinov’eva I.V., Zakhodyaeva Y.A. et al. // Metals (Basel). 2021. V. 11. № 12. P. 1964. https://doi.org/10.3390/met11121964
  20. Зиновьева И.В., Федоров А.Я., Милевский Н.А. и др. // Теорет. основы хим. технологии. 2021. Т. 55. № 4. С. 480. https://doi.org/10.31857/S0040357121040199
  21. Kozhevnikova A.V., Zinov’eva I.V., Zakhodyaeva Y.A. et al. // Processes. 2022. V. 10. № 12. P. 2671. https://doi.org/10.3390/pr10122671
  22. Dong L., Li Y., Shi P. et al. // J. Power Sources. 2023. V. 582. P. 233564. https://doi.org/10.1016/j.jpowsour.2023.233564
  23. Binnemans K., Jones P.T. // J. Sustain. Metall. 2023. V. 9. № 2. P. 423. https://doi.org/10.1007/s40831-023-00681-6
  24. Kadachi A.N., Al-Eshaikh M.A. // X-Ray Spectrometry. 2012. V. 41. № 5. P. 350. https://doi.org/10.1002/xrs.2412
  25. Iwai M., Majima H., Awakura Y. // Hydrometallurgy. 1988. V. 20. № 1. P. 87. https://doi.org/10.1016/0304-386X(88)90028-X

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML
Baixar

Declaração de direitos autorais © Russian Academy of Sciences, 2024