Determination of Conditions for Selective Sorption of Silver(I) on Thiocarbamoylated Polyethylene

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

Sorption properties of thiocarbamoylated polyethylene with respect to silver(I) from multicomponent solutions have been studied. It was found that the synthesized sorbent is characterized by a high sorption capacity and selectivity with respect to silver ions. In the static sorption mode, quantitative extraction is possible from solutions with a concentration of Ag(I) 1 · 10–4 mol/dm3 in the pH range from 1 to 7, with concomitant Ca(II), Mg(II), Cu(II), Fe(III), Zn(II), Cd(II), Ni(II), Mn(II), Co(II), Pb(II) have no effect on the degree of extraction of silver ions. The high selectivity of sorption is maintained under dynamic conditions in the presence of excessive amounts of base metal ions at pH 2. The total dynamic sorption capacity for silver is 0.35 mmol/g (solution transmission rate 2 cm3/min, pH 2, sorbent weight 0.1 g, C = 1 · 10–4 mol/dm3). The composition of the eluents providing the highest values of the degree of desorption of silver from the surface of the sorbent has been determined. It was found that during sorption using a sorbent after the sorption-desorption stage, its silver capacity decreases slightly.

全文:

受限制的访问

作者简介

E. Melnik

UNIIM – Affiliated Branch of the D. I. Mendeleyev Institute for Metrology; Ural Federal University named after the first President of Russia B.N. Yeltsin (UrFU)

编辑信件的主要联系方式.
Email: ea-melnik@mail.ru
俄罗斯联邦, Yekaterinburg, 620075; Yekaterinburg, 620002

Y. Petrova

UNIIM – Affiliated Branch of the D. I. Mendeleyev Institute for Metrology

Email: ea-melnik@mail.ru
俄罗斯联邦, Yekaterinburg, 620075

L. Neudachina

Ural Federal University named after the first President of Russia B.N. Yeltsin (UrFU)

Email: ea-melnik@mail.ru
俄罗斯联邦, Yekaterinburg, 620002

A. Pestov

Ural Federal University named after the first President of Russia B.N. Yeltsin (UrFU); I.Ya. Postovsky Institute of Organic Synthesis of the Ural Branch of the Russian Academy of Sciences

Email: ea-melnik@mail.ru
俄罗斯联邦, Yekaterinburg, 620002; Yekaterinburg, 620137

V. Osipova

I.Ya. Postovsky Institute of Organic Synthesis of the Ural Branch of the Russian Academy of Sciences

Email: ea-melnik@mail.ru
俄罗斯联邦, Yekaterinburg, 620137

参考

  1. Calisi А., Lorusso C., Gallego-Urrea J.A. et al. // Sci. Total Environ. 2022. V. 851. P. 158113. https://doi.org/10.1016/j.scitotenv. 2022. 158113
  2. Sim W., Barnard R.T., Blaskovich M.A.T. et al. // Antibiotics. 2018. V. 7. № 4. P. 93. https://doi.org/10.3390/antibiotics7040093
  3. Borah D., Das N., Sarmah P. et al. // Mater. Today Commun. 2023. V. 34. P. 105110. https://doi.org/10.1016/j.mtcomm.2022.105110
  4. Khatabi H., Bidoki S.M., Haji A. // Mater. Chem. Phys. 2022. V. 290. P. 126548. https://doi.org/10.1016/j.matchemphys.2022.126548
  5. Singh C., Anand S.K., Upadhyay R. et al. // Mater. Chem. Phys. 2023. V. 297. P. 127413. https://doi.org/10.1016/j.matchemphys.2023.127413
  6. Yu S., Yin Y., Liu J. // Environ. Sci.: Processes Impacts. 2013. V. 15. P. 78. https://doi.org/10.1039/C2EM30595J
  7. Morgan T.P., Wood C.M. // Environ Toxicol Chem. 2004. V. 23. № 5. Р. 1261. https://doi.org/10.1897/03-181
  8. Bilberg K., Malte H., Wang T. et al. // Aquat. Toxicol. 2010. V. 96. № 2. P. 159. https://doi.org/10.1016/j.aquatox.2009.10.019
  9. Botelho M.T., Passos M.J.A.R.C., Trevizani T.H. et al. // Mutat. Res., Genet. Toxicol. Environ. Mutagen. 2022. V. 881. P. 503527. https://doi.org/10.1016/j.mrgentox.2022.503527
  10. Andreï J., Guérold F., Bouquerel J. et al. // Aquat. Toxicol. 2023. V. 256. P. 106421. https://doi.org/10.1016/j.aquatox.2023.106421
  11. Xiang Q.Q., Kang Y.H., Lian L.H. et al. // Aquat. Toxicol. 2022. V. 252. P. 106318. https://doi.org/10.1016/j.aquatox.2022.106318
  12. Yeo M.K., Kang M. // Bull. Korean Chem. Soc. 2008. V. 29. № 6. P. 1179. https://doi.org/10.5012/bkcs.2008.29.6.1179
  13. Padhye L.P., Jasemizad T., Bolan S. et al. // Sci. Total Environ. 2023. V. 871. P. 161926. https://doi.org/10.1016/j.scitotenv.2023.161926
  14. Islam M.A., Dada T.K., Parvin M.I. et al. // J. Water Process Engineer. 2022. V. 48. P. 102935. https://doi.org/10.1016/j.jwpe.2022.102935
  15. Петрова Ю.С., Алифханова Л.М.К., Кузнецова К.Я. и др. // Журн. неорган. химии. 2022. Т. 67. № 7. С. 991.
  16. Корнейков Р.И. // Неорган. материалы. 2021. Т. 57. № 4. С. 437.
  17. Алифханова Л.М.К., Петрова Ю.С., Босенко С.Н. и др. // Журн. неорган. химии. 2021. Т. 66. № 4. С. 540.
  18. Çelik Z., Gülfen M., Aydın A.O. // J. Hazard. Mater. 2010. V. 174. № 1–3. P. 556. https://doi.org/10.1016/j.jhazmat.2009.09.087
  19. Maleki H., Durães L., Portugal A. // J. Non-Cryst. Solids. 2014. V. 385. P. 55. https://doi.org/10.1016/j.jnoncrysol.2013.10.017
  20. Ladhe A.R., Frailie P., Hua D. et al. // J. Membr. Sci. 2009. V. 326. № 2. P. 460. https://doi.org/10.1016/j.memsci.2008.10.025
  21. Herman P., Pércsi D., Fodor T. et al. // J. Mol. Liq. 2023. V. 387. P. 122598. https://doi.org/10.1016/j.molliq.2023.122598
  22. Melnyk I.V., Vaclavikova M., Ivanicova L. et al. // Appl. Surface Sci. 2023. V. 609. P. 155253. https://doi.org/10.1016/j.apsusc.2022.155253
  23. Liu P., Wang X., Tian L., et al. // J. Water Process Engineer. 2020. V. 34. P. 101184. https://doi.org/10.1016/j.jwpe.2020.101184
  24. Losev V.N., Elsufiev E.V., Buyko O.V. et al. // Hydrometallurgy. 2018. V. 176. P. 118. https://doi.org/10.1016/j.hydromet.2018.01.016
  25. Thomas H.C. // J. Am. Chem. Soc. 1944. V. 66. № 10. P. 1466.
  26. Родионова А.П., Землякова Е.О., Корякова О.В. и др. // Известия АН. Сер. Химическая. 2019. № 6. С. 1248.
  27. Zhang L., Zhao Y., Mu C. et al. // Sustainable Chem. Pharm. 2020. V. 17. P. 100287. https://doi.org/10.1016/j.scp.2020.100287
  28. Ghanei-Motlagh M., Fayazi M., Taher M.A. et al. // Chem. Eng. J. 2016. V. 290. P. 53. https://doi.org/10.1016/j.cej.2016.01.025
  29. Akhond M., Absalan G., Sheikhian L. et al. // Sep. Purif. Technol. 2006. V. 52. P. 53. https://doi.org/10.1016/j.seppur.2006.03.014
  30. Yang T., Zhanga L., Zhong L. et al. // Hydrometallurgy. 2018. V. 175. P. 179. https://doi.org/10.1016/j.hydromet.2017.11.007
  31. Safarpour M., Safikhani A., Vatanpour V. // Sep. Purif. Technol. 2021. V. 279. P. 119678. https://doi.org/10.1016/j.seppur.2021.119678
  32. Мельник Е.А., Сысолятина А.А., Холмогорова А.С. и др. // Эталоны. Стандартные образцы. 2022. Т. 18(2). С. 57. https://doi.org/10.20915/2077-177-2022-18-2-57-71
  33. Kinnunen V., Perämäki S., Matilainen R. // Spectrochim. Acta. Part B. 2022. V. 193. P. 106431. https://doi.org/10.1016/j.sab.2022.106431

补充文件

附件文件
动作
1. JATS XML
下载
2. Supplement
下载 (222KB)
索引源数据
3. Fig. 1. The effect of the acidity of the medium on the sorption of silver ions from a multicomponent system. 1 – C = = 1 × 10-4 mol/l, C = 4 × 10-4 mol/L; 2 – C = = 1 × 10-4 mol/L, C = 1 × 10-4 mol/l; msorbent = = 0.0100 g, d < 0.071 mm.

下载 (67KB)
索引源数据
4. Fig. 2. Silver sorption isotherm(I) – and the results of its processing by mathematical models. C = 1 × × 10-4 mol/l; msorbent = 0.0100 g, d < 0.071 mm, pH 2.

下载 (215KB)
索引源数据
5. 3. Dynamic output curves of metal ion sorption on thiocarbamoylated polyethylene: msorbent = = 0.1000 g (1), 0.0500 g (2); 0.0100 g (3); C = 1 × 10-4 mol/l; C = 8 × 10-4 mol/l; 0.125 mm > d > 0.100 mm, the transmission rate of the model solution is 2 cm3/min, pH 2.

下载 (171KB)
索引源数据
6. Fig. 4. Dependence of the degree of silver extraction(I) on the volume of the passed solution, sorbent = 0.1 g (a), 0.05 g (b). 1 – the first sorption cycle; 2 – the second sorption cycle; 3 – the third sorption cycle. C = 1 × 10-4 mol/l; C = 8 × × 10-4 mol/l; 0.125 mm > d > 0.100 mm, the transmission rate of the model solution is 2 cm3/min, pH 2.

下载 (282KB)
索引源数据

版权所有 © Russian Academy of Sciences, 2024